AbstractThere is no doubt that the type and properties of cement extremely affect the general properties of produced concrete .Cement is one of the main ingredients of cement past phase in concrete. In present study chemical and physical properties of four types of Portland cement available in Iraqi local market were studied ,these types as follow : two types of ordinary Portland cement Kubaisa (Iraqi cement) and Ismnta (Jordanian cement) and the others of sulfate resisting cement Torab alsabia (Lebanese cement ) and Al-qaim (Iraqi cement).Chemical analysis of the four types of cement were conducted in Baghdad central laboratory in National Center for Constructional Laboratories and Researches (NCCLR) and Al-qaim factory laboratory .The physical tests were conducted in the concrete laboratory of Al_anbar university-college of engineering including standard cement paste ,initial and final setting and compressive strength of cement mortars.The results indicate that the local cement (Kubaisa and Al-qaim) showed better performance than imported cement (Ismnta and Torab alsabia) in most tested chemical and physical properties .Kubaisa cement showed 34.1 % , 35.5 % higher compressive strength compared with Ismnta cement at 3 and 7 day respectively and lower loss on ignition and insoluble residue . The major compounds of Kubaisa cement were nearest to those in typical cement. For sulfate resisting cement , Al-qaim cement showed 13.3 % higher compressive strength at 7 day and lower percentage of C3A (1.95%) . Torab alsabia cement exceed the limits of Iraqi standard I.O.S No.5 1984.
This work study the effect of partial replacement of cement by hydrated cement on some properties of cement paste and cement mortar such as normal consistency, initial and final setting time, compressive strength, and length change. The results show that pastes containing hydrated cement require more water than reference paste to give normal consistency. The results also show that the replacement by hydrated cement delay the initial and final setting time of cement paste. The delay in setting time increased with increasing the partial replacement by hydrated cement. Compressive strength test was carried out on (54) cubes of (50) mm side dimensions of mortars containing (5, 10, 15, 20, and 25%) of hydrated cement at (3, 7, and 28) days. They were then compared with reference mortar. The compressive strength results show that the compressive strength decreases with increasing the replacement percentage by hydrated cement at all ages. The decreases in compressive strength reached (23.05 %) when (25%) of cement was replaced by hydrated cement in (28) days. The results also show that the replacement of cement by hydrated cement increases the length change of mortars compared with reference mortar.
In this study practical tests for thermal conductivity are done on twenty one specimens for seven types of cement mortar contains different types of cement available in local markets for Kirkuk city in the same standard conditions. Heat flow amounts within the specimens are calculated using Fourier law for conduction. Comparison between practical results and theoretical values depended in references for calculating thermal loads in concrete walls gave good agreement. Test results for specimen No. (7) for cement of Al-Sulaimanya company gave minimum value for thermal conductivity, which was (1.162 W/m.oC), and maximum value was for specimen No. (4) for Iranian cement, which was (1.55 W/m.oC) and for specimen No. (3) for cement of Bazian company, which was (1.52 W/m.oC). Results of thermal conductivity for all the other specimens were within the depended theoretical value. Minimum heat flow within the material was for specimen No. (7) for cement of Al-Sulaimanya company, while maximum value was for specimen No. (4) for Iranian cement. Key words: thermal conductivity test, cement, mortar, heat flow, Fourier law for conduction.
Abstract :- For improving the properties of asphaltic cement several materials such as sulfur, rubber, carbon black, polymers….etc. are used for this purposes. In this study low density Polyethylene (LDPE) used at different percentage (0%, 1%, 3%, 5% and 7%) by weight of the asphaltic cement and then the changes in the properties are evaluated by pentration test (ASTM D-5), softening point test (ASTM D-2398), and Kinematics viscosity test (ASTM D-2170). Temperature susceptibility was evaluated by using Penetration vescosity number ( P.V.N ). In addition to that stiffness modulus of asphalt cement was predectied by using van der pole’s nomograph. The study showed that the LDPE increase the hardening of asphalt cement at different percentage except at (1%), and decrease the susceptibility of asphaltic cement to temperature.
Concrete is produced from millions of tons of Cement, which emits a significant amount of carbon dioxide from cement mills and contributes to global warming. Therefore, it is important to seek out less expensive and more environmentally friendly substitutes for OPC. While various substitutes are available, such as recycled glass, marble, silica fume fly ash, or agricultural waste like rice husks or wheat straw, the performance of concrete is significantly affected when bentonite is used as a replacement for Cement. This study aims to evaluate Jhelum bentonite, which is located at 32°56′ north and 73°44′ east longitude, as a replacement for Cement in different ratios (0:100, 10:90, 20:80, 30:70, and 40:60) to improve the durability of the system as more bentonite is used to replace conventional Portland cement, the workability, density, and water absorption of the new concrete all decrease. Compressive Strength, Tensile Strength, and flexural Strength of blocks and cylinders were tested after being cured for 7 and 28 days. Analysis of these strength tests revealed that the mixes containing bentonite were weaker after 7 days compared to 28 days, and the Strength of blocks was reasonable compared to cylinders.Keywords: Bentonite, Concrete, Compressive Strength, Tensile Strength.
The aim of this research is to produce lightweight cement mortar with properties better than reference ordinary cement mortar. Porcelanite stone were utilized as lightweight aggregate with a volumetric partial substitution of fine aggregate. The process includes using different percentages (5, 10, 15 and 20 %) of pre-wetted (24hr.) porcelanite to produce lightweight mortar with internal curing. Water curing was used for reference mortar mixture and air curing for the other mixtures of porcelanite substitution. Compressive strength, flexural strength, density and ultrasonic pulse velocity for different ages (7, 14 and 28 days) have been tested. The results show an improvement in the properties of cement mortar especially in replacement percentage of 10 %.
1-AbstractThis research includes the variation effect of (W/C) water: cement ratio on the properties as compressive strength , flxural strength , density and workability of concrete contains low Polymer SBR ratio.1:2:4 (cement: sand :gravel) by weight mixes were used . The polymer was added as percentages of cement weight and it was 2%. Reference mix was made. Water cement ratio (w/c) were used are 0.2 , 0.3 , 0.4 , 0.5 and 0.6 respectively and 0.35 (w/c) was used for reference mix . The density of concrete varied between 2030 kg/m3 and 2360 kg/m3.
This main aim of this study is evaluate wide range of fresh and hardened properties of sustainable self-compacting concrete containing various types of Cement Replacement Materials with optimum contents of Polyethylene Terephthalate PET waste plastic as fibers and fine aggregate replacement. This is to evaluate effect of the two forms of PET and to determine the best CRMs could be used with sustainable SCC. such as limestone, glass powder and fly ash with high replacement rate of 70% by weight of cement were used while fourth one (kaolin) was used with replacement rate of 20%. PET fibers were added to SCC with an aspect ratio of 24.4 and 0.7% volume fraction whereas fine aggregate partially replaced by 4% of waste plastic. Four reference mixtures contained FA, LP, GP and KA only, same four mixtures contained 0.7% PET fibers by volume, and the other same four mixtures contained 4% PET fine aggregate by volume. The obtained results all tested fresh properties, which include slump flow, T500, L-Box and segregation resistance were within the limits of the specification reported in EFNERC guidelines. Further, the forms PET have an adverse effect fresh properties of SCC. As for hardened properties (compressive strength, splitting tensile strength, flexural strength and impact strength). Further, this produced type of SCC showed an range of compressive strength (15.2-31.64 MPa) at 28 days. It can be from the current study the best CRMs to be used in SCC containing PET wastes was FA in terms of most tested properties.
Fresh and hardened properties of self-compacting concrete was experimentally examined by replacing different percentages of cement by soft clay powder, which resulting from crushing the wastes of clay bricks. Three percentages (5%, 10%, and 15%) of cement were replaced with clay powder to study their effect on the properties of cement mortar and concrete of Grade (C35) in both fresh and hardened states. It was found that development rates of the compressive and tensile strengths for the mortar between ages of 7 to 28 days, decreased with increasing the percentage of the clay powder. Compared to the mix without clay powder, it was found that replacing (5%) from the cement causes a significant increase in the workability of the self-compacting concrete and the properties of the resulting hardened concrete such as compressive strength, tensile strength, and modulus of elasticity. While using (10%) and (15%) of the clay powder causes a significant decrease in the workability of the fresh concrete and the properties of the hardened concrete compared to mix without clay powder.
This research includes study the effect of fineness upon physical properties of cement mortar where use ordinary Portland cement with fineness (300 m2/kg) as reference mixture which denoted by symbol (M1), and then produce with flowing fineness (350,400,450 and 500 m2/kg) which denoted by ( M2, M3, M4, M5 ) respectively . The results of study show that increasing in fineness makes an increase in water quantity that requires for consistence of standard paste and the ratio of above mixes with reference mixture (2%,5%,7%,11%)respectively, although the increasing in density for all ages and increasing in compressive strength in early age, the increasing ratio in 3 days age was ( 45% , 50% , 60% , 70%)respectively .this increasing in fineness makes increasing in ratio of flow as compared with reference mix(16%, 25%, 50%, 66%) respectively
The most concerning issue confronting the planet these days is the ascent in Carbon dioxide (CO2) levels to record levels. The cement industries are answerable to between 6-8 % of worldwide CO2 emitting. In construction sectors, researchers tried to contribute in decreasing of CO2 in atmosphere produced by industry and using that was released in air. Accelerated CO2 curing is one of the methods used to get benefit from CO2 in the air. In this paper, CO2 concentration in addition to pressure, relative humidity and period of curing all had a significant influence upon the features of Cement – Based Composites. Results showed that using CO2 curing with different and specific properties of fibers (types, quantities, circumstances and lengths) improved the most mechanical properties and enhanced durability such as: strength, stiffness, ductility, toughness, porosity, and absorption.
Abstract The use of no fines concrete in construction increased especially during and after 1970s. New concrete is obtained from no-fines concrete in this research by adding Styrene Butadiene Rubber (SBR) Polymer as a ratio of cement content. This research includes the study of the effect of SBR polymer on stress-strain relationship of concrete under compression. The concrete mixes by weight were (1:7, 1:6, 1:5, and 1:4) cement / aggregate (C/A). The polymer was added as percentages by weight of cement as (5, 7.5 and 10%). Rreference mixes were made for every case. A new mathematical model for both ascending and descending portions is suggested in this research and discussed. The area under the stress strain curve was found in polymer modified no-fines concrete to be greater than reference concrete and was increased with polymer / cement ratios (P/C). The suitability of no fine polymer concrete to be used in structural members has been affirmed in this research especially for (1:4 and 1:5) C/A polymer mix.
ABSTRACT: In this paper, artificial neural networks (ANNs) are used in attempt to obtain the strength of polymer-modified concrete (PMC). A database of 36 case records is used to develop and verify the ANN models. Four parameters are considered to have the most significant impact on the magnitude of (PMC) strength and are thus used as the model inputs. These include the Polymer/cement ratio, sand/cement ratio, gravel/cement ratio, and water/ cement ratio. The model output is the strength of (PMC). Multi-layer perceptron trained using the back-propagation algorithm is used. In this work, the feasibility of ANN technique for modeling the concrete strength is investigated. A number of issues in relation to ANN construction such as the effect of ANN geometry and internal parameters on the performance of ANN models are investigated. Design charts for prediction of polymer modified concrete strength are generated based on ANN model. It was found that ANNs have the ability to predict the strength of polymer modified concrete, with a very good degree of accuracy. The ANN models developed to study the impact of the internal network parameters on model performance indicate that ANN performance is reality insensitive to the number of hidden layer nodes, momentum terms or transfer functions. On the other hand, the impact of the learning rate on model predictions is more pronounced.keywords:; Artificial Neural networks; Strength; Polymer Modified Concrete; Modeling.
Slurry infiltrated fiber concrete (SIFCON) is a relatively new high performance material and can be considered a special type of fiber concrete (FRC) with high fiber content. The matrix consists of a flowing mortar or cement slurry that must penetrate well through the network of fibers placed in the mold. SIFCON has excellent mechanical properties combined with high ductility and toughness values. SIFCON a relatively new material, is composed of mud (cement or cement and sand), water, a plasticizer (water reducer), and fibers. All previous studies have used waste steel fibers, steel fibers and other fibers, but in this study, plastic fibers were made from polyethylene terephthalate (PET) by cutting carbonated beverage bottles. The main objectives of this study are: Determination the effect of the waste plastic fiber volume ratio on the strength and deformation of (SIFCON) samples under the influence of bending loads. Both flexural strength and toughness properties were determined by testing samples (100×100×400) mm at 28 and 56 days of age. The results obtained from these tests were compared with those performed on conventional tests. Aspect Ratio equal to (36.8) and three volume ratios (3%, 5% and 7%) of the total volume of the concrete mixture were used to add fibers with different volume ratios. A conventional concrete mix was created as a reference for comparison. Bending strength and fresh concrete tests were performed. And compared with the reference mixture and according to the analysis of the results. The results showed an improvement in bending strength .It was found through the flexural examination that the flexural strength of the mixture containing fiber percentage (7%) achieved the highest strength compared to the rest of the ratios used, compared with the reference mixture (Ref.) by (32.25, 27.5)% for ages (28, 56), respectively.
This paper presents and discuses some properties of self-compacting concrete SCC containing optimum contents of different types of cement replacement materials CRMs like fly ah, silica fume and limestone powder. The purpose is to evaluate the performance of SCC mixtures to choose the best one for strengthening purposes of corroded reinforcement concrete beams. In a preliminary work, the theoretical optimum contents of the above materials were specified using statistical program (Minitab) and they were verified experimentally. This verification based on checking fresh properties such as slump flow, T500, L-box and segregation resistance as well as compressive strength. The optimum contents of CRMs: 14% fly ash, 19% limestone, 18% silica fume plus fly ash and 11% silica fume were selected and studied. Compressive, tensile, and flexural strengths were examined, as well as the modulus of elasticity, water absorption and porosity (which reflect the related durability properties) were examined. Test results show that the optimum verified theoretical percentage of a combination of fly ash and silica fume, at 18% by weight of cement with a fixed water-binder ratio of 0.33 showed the best overall performance. It was deduced that this SCC mix gave the highest mechanical properties and the lowest porosity and water absorption. For example, the compressive strength increased by 36.25% as compared to SCC mix containing limestone powder. Further, the porosity and water absorption decreased by 120.8% and 164% respectively as compared to the above same SCC mix. Thus, it could be used for strengthening purpose of corroded RC beams.
The problem of solid waste is being emerged increasingly due to the increased quantity of solid waste as a result of population’s increase .From the point of view of environmental and energy concerns, it is preferable to reuse the organic and inorganic components of solid waste in order to minimize the cost. In this investigation, the possibility of using solid waste ash (SWA) as a partial replacement of cement and its effect on the mechanical properties of concrete was studied. Samples of municipal solid wastes were collected were burring and changed to ash. A total of 50 cubes, 15 small cubes, and 30 cylinders, as well as 5 prisms were prepared .Various properties of solid waste ash are added to the cement mistures with percent's of 5, 10, 15 and 20 percent by weight of solid waste ash. A concrete mix with a percent solid waste ash was used as reference. Pozzolanic activities of all mortars, and setting times of all pastes, and workability of all mixes were investigated .Compressive strength, splitting tensile strength, absorption, and drying shrinkage for reference for reference and solid waste concrete specimens were investigated at various ages. Results demonstrate that the pozzolanic activity was within ASTM requirements for the cases of 5% and 10% ash replacement. For 15 and 20 percent replacement this activity was only slightly less than the ASTM value. The 90-day compressive strength rose, in comparison with control specimens, with 5 percent replacement and was only slightly lower at 10 percent replacement. In splitting tensile strength was at least equal to reference specimens for all replacement ratios. The rise in these values, over the reference specimens, ranged between 0 to 21 percent for the case of 20 and 5 percent replacement, respectively.
Collapse of gypseous soils may cause excessive settlement and serious damage to engineering structures. Various improvement approaches, such as mechanical techniques and chemical additions, have been used to reduce the collapsibility of these soils. The odometer test has traditionally been used to assess the collapsibility of the improved gypseous soils; however, because the small size of test specimens, this method may not adequately reflect field conditions. In this research, a laboratory model test of 600 x 600 x 600 mm with a model footing of 100 x 100 mm was developed to measure the collapse characteristics of a gypseous soil. The top layer underneath the footing was improved by compaction, cement kiln dust (CKD), geogrid, and a combination between CKD and geogrid. The top layer was improved at two values of thickness of 50 and 100 mm. The results obtained from this study indicate that the values collapsibility settlement reduction factor for compacted soil and the soil treated with CKD were 75 and 82%, 89% receptively. These values increased up to 95 % when a combination of CKD and geogrid was applied. As discussed herein, the aforementioned treatment methods can effectively be used to improve the collapsibility of gypseous soils.
This research work includes production of new type of light weight concrete and studies the mechanical and thermal properties. Several proportions of raw materials were used to produce this type of concrete. This study is intended to produce light weight concrete with low thermal conductivity so that it can be used for concrete masonry units. Polystyrene aggregate was added as percentages by weight of cement to improve the thermal properties of this type of concrete .Mechanical , and thermal tests with difference ages were made in this work .For polystyrene concrete with polystyrene cement ratio (p/c) of (2.67 – 6 )% , the28-day compressive strength range is from (4.31 – 2.67)MPa, flexural strength range is from (3.05-1.719 ) MPa , density range is from ( 1493-1213 ) kg/m 3 ,and thermal conductivity range is from ( 0.91-0.782)% as a percentage by that of reference mix. The study show suitability of this type of concrete to be used in concrete masonry units of non-bearing walls.
AbstractThis study aims to investigate the properties of SCC produced by locally availablematerials , and attempts have been made to increase the range of grading of fineaggregate, with fineness modulus ranging from (1.5 to 4.1) , and to study the effect of themaximum size of coarse aggregate . It also aims to study the influence of High ReactivityMetakaolin (HRM) as a partial replacement by weight of cement on the properties of freshand hardened SCC, 24 different mixes of SCC are prepared .8 mixes are considered asReference mixes which are used for comparison purposes. To determine the workability,different test methods were adopted such as slump flow, V-funnel, and L-box tests. Whenfineness modulus of fine aggregate and maximum size of coarse aggregate increase,flowability, passing ability and segregation resistance decrease as compared with smallmaximum size of aggregate and other fineness modulus. Further more, the inclusion of10% HRM as a partial replacement by weight of cement leads to decrease flow ability andincrease of viscosity. The fineness modulus (3.1) of fine aggregate gives better resultsthan other fineness modulus. The results obtained from this study, also show that it ispossible to produce SCC from local available materials which satisfy the requirement ofthis type of concrete. Moreover, the results show the possibility of using different gradingof fine aggregate with fineness modulus ranging from (1.5 to 4.1) and the effect ofchange in fineness modulus is not significant on hardened concrete properties , while it ismore significant on fresh concrete properties .
ABSTRACT:The resistance of concrete to sulfate attack is considered as one of the important factors for concrete durability.The effect of SBR polymer on sulfate resistance of concrete is investigated. Both internal and external sulfate attack are considered.Internal sulfate attack was made by adding gypsum to raise the sulfate content of sand to that of Ramadi city soil (2.17%), while the external sulfate attack was made by adding chemical materials (MgSO4.7H2O, Na2SO4, CaCl2.2H2O, NaCl) to tap water to convert it into water similar to groundwater of Ramadi city.The laboratory tests were compressive and flexural strength, modulus of elasticity, slump, ultra-sound velocity and total percentage of sulfate after exposing to attack for different ages. It was found that the compressive strength of reinforced normal concrete (RNC) for ages (7,28,90,180) days respectively were (20,28,11.166,7) MPa, the compressive strength of polymer Portland cement concrete( PPCC) with polymer/cement ratio( P/C)=5% (PPCC5) were (21.83,32.666,12.766,8.733) MPa and for PPCC with (P/C)=10% were (24.166,35.866,15.533,11.366)MPa.While the flexural strength of RNC for different ages (7,28,90,180) respectively were (3.953,3.7,1.68,11.305) MPa, the flexural strength of PPCC5 were (4.05,5.025,2.13,1.605) MPa and for PPCC10 were (4.43,6.375,2.43,1.92) MPa.The static modulus of elasticity at age (28) days for (RNC) was (37.4) GPa , for PPCC5 was (9.7) GPa and for PPCC10 was (13.63) GPa.Slump for (RNC) was (155) mm, for PPCC5 was (142) mm and for PPCC10 was (75) mm.T he ultra-sound velocity of RNC for ages (7,28,90,180) respectively were (4.2,4.445,4.203,4.53) Km/sec , for PPCC5 were (4.36,4.646,4.53,4.176) Km/sec and for PPCC10 were (4.437,4.837,4.656,4.52) Km/sec.It was found that (PPCC10) has higher resistance to sulfate attack than (PPCC5) and (NRC). The thesis refers to necessity of polymer to improve the resistance of concrete to sulfate attack although if the sulfate percentage raise to more than (0.5) % which represents the maximum limit of sulfate percentage in I.O.S No. 45-1970.
The gypseous soils are distributed in many locations in Iraq. The Engineering properties of such soil will be changed when it is wetted and it leads to failure which causes danger on the structures built on. This reason needs to study its properties and to find the way to treat it. In this study, natural properties of soil prepared from Samarra-Salah al deen governorate were studied. The gypsum content of soil is about 32%. To improve this soil, many trials were carried out on the soil by additive of Portland cement and calcium chloride. For the importance of the compressibility of the soil, the effect of the additives were studied and it is found that addition of 3% of cement or 5% of calcium chloride will improve the soil compressibility.
The paper shows the final findings of the effect of metakaolin on the strengths properties of concrete exposed to crude oil. Sulfate resistance Portland cement of V type was used and specimens of concrete were adjusted and subjected to a solution of concentrated crude oil. However, the samples are cured in a control media at immersion ages of (28, 56 & 120 days) with ambient temperature, then samples have been kept in curing water for comparisons purpose as well. The results explain that the use of metakaolin reinforces compressive, flexural and splitting resistance of concrete which is exposed to crude oil. The compressive strength reduction increased from 8.0% at (28 days) to 37.7% at (120 days) curing for normal weight concrete (NW) whereas the concrete incorporating metakaolin (MC) has a reduction of 6.0% at (28 days) & 29.3% at (120 days). .
The performance of the structural materials (concrete and steel reinforcement) and the behavior of the structural members after they were exposed to high temperatures have been considered the main topics of the current literature review. All varieties of concrete mixtures lost their compressive strength after 300˚C, even though there was no discernible strength loss between 150 and 300˚C. It was also discovered that the heating time had no appreciable impact on the strength loss when the exposed to heat less than 300 ˚C. Above 300 ˚C. Concrete begins to lose strength after being exposed for longer than one hour; the greatest loss of strength occurs during the first and second hours of exposure. Both the cured cement paste and the aggregates undergo chemical and physical changes at temperatures ranging from 600 °C to 900 °C. The 5% weighted rice husk ash (RHA) blended concrete still had an advantage in compressive strength, over the concrete when subjected to temperatures up to 700 C for two hours. Adding more recycled glass and ceramic particles to regular concrete increases its overall compressive and tensile strengths. Concrete becomes more durable and has fewer cracks when there is a higher replacement rate for ceramic and glass particles. The splitting tensile strength decreased with increasing temperature, changing from 60% to 70% of its initial strength after 600 °C. In this review, the better performance of concrete than the other concrete in terms of mechanical, physical, and durability properties at both room temperature and high temperature were concrete with 10% waste glass powder (WGP) substitution as a partial of cement and 10%–20% crushed glass (CG) substitution as a partial of aggregate .
SIFCON is a relatively new material and consists of slurry (cement or cement and sand), water, super plasticizers (water reducers) and fibers. In all previous research, steel fibers and other types of fibers were used, but in this study, waste plastic fibers Polyethylene Terephthalate (PET) created by cutting carbonated beverage bottles were used for the first time in the production of SIFCON. Three volume ratios (3%, 6% and 10%) of the total volume of the concrete mixture were used to add fibers in different volume ratios, and a reference concrete mixture was created for comparison. Tests of compressive strength, impact resistance, ultrasound transmission velocity check and other tests were performed on the constructed models. Compared with the reference concrete, according to the analysis of the results. The results showed an improvement in the compressive strength it increased by (18.5%), an increase in the impact resistance by (416.67%), and a decrease in the velocity of ultrasound by (19.42%).
Abstract:This research studies the effect of high temperature which is reached to 600 °C onstructural lightweight and normal weight concrete. Lightweight concrete mix designedaccording to ACI committee 211-2-82 with mix proportion 1:1.12 :3.35 by volume .Thewc ratio equal to 0.5 by weight and cement content 550 kgm3. Mix proportions ofnormal weight concrete were 1:2:3 by weight with cement content 400 kgm3 and samewc. The design compressive strength at 28 days of normal weight concrete (NWC) andlightweight concrete (LWC) were 34.7 MPa and 22.62 MPa respectively. Compressivestrength tests were performed on 100 mm cubes exposed to high temperature 100,200,400and 600 °C. The normal weight concrete and light weight concrete test specimens wereexposed to high temperature for 10 minute suddenly at the required degree. Moreover,light weight concrete test specimens tested after graduate exposure to high temperaturereaching to the required degree with and without drying to examine the effect of moisturecontent.The results indicated that the structural lightweight concrete exhibits approximatelysimilar compressive strength loss compared to normal weight concrete up to 600 °C at 28days in graduate exposure .The percentage of reduction on compressive strength was30% in lightweight concrete compared to 28% in normal weight concrete at 600 °C .Insudden exposure to high temperature ,the opposite behavior was noticed .The percentageof reduction on compressive strength was 64.4% in lightweight concrete at 600°C .Drying of lightweight concrete specimens before graduate exposure to high temperaturessignificantly reduce the loss of compressive strength.
There are various means of recycling agricultural wastes to maximize economic benefit from it. According to environmental statistics, agricultural wastes is one of the most dangerous types of wastes, especially in villages, because it is disposed of by burning. In this study, production of natural ash from agro wastes was carried out. Two types of agro waste ash were produced through burning and grinding process. waste date tree and waste reeds ash. The waste date ash (WDA) and waste reeds ash (WRA) were included in concrete by replacement of a specific portion of cement weight (5%, and 10%). Moreover, a blend of the two types of ashes were also considered. Furthermore, the natural ash was utilized in production of green concrete. Hardened density and compressive strengths at various ages (7, 28 and 56 days) were evaluated. The results in this research showed an excellent increase in compressive strength at ages (7,28 and 56) days. When measuring the compressive strength at the late age (56 days), DPA + WRA it was the best model used if it recorded the highest increase in it. Also, the use of WRA10% gave a good result, increasing its strength of the reference mixture and the rest of the mixtures also gave good and remarkable results in increasing the resistance, as the use of ash in these mixtures protects the environment from pollution and gives mixtures of higher resistance and can be used as a partial substitute for cement, except for DPA10%, so the usual mixture was better than it.
The Impact of silica fume existence and its content with the duration of curing on concrete compressive strength (ordinary and high) has investigated experimentally. Two mixture sets were done in this work to examine the concrete ordinary and high strength. Every set involved four mixtures with varied silica fume proportions as a substitution of cement with (0, 5, 10 and 15 percent). Ninety-six cubes of concrete were prepared and cured by immersion in water to the required age (7, 28, 90 and 150 days). In ordinary concrete and high strength concrete, the results demonstrate that when silica fume used as a substitution with 15 %, the compressive strength of concrete gave the highest value. As compared with concrete having nil content of silica fume, the earned strength for high compressive concrete consisting of silica fume was relatively less than the corresponding ordinary concrete strength. However, continuously curing with water after 28 days produced a considerable increase in the compressive strength of concrete; such an increase in compressive strength was greater in the existence of silica fume
AbstractThis study deals with establishing high-velocity impact properties of polymer –modified concrete (PMC) including Styrene-Butadiene rubber (SBR), with different weight ratios of polymer to cement: 4%, 8% and 12%. Steel fibers were also included. Sixteen (500mm) diameter, (50mm) thick discs for high-velocity impact tests were used. In addition compressive strength, splitting tensile strength, and flexural strength (modulus of rupture) were companionly recorded. In all the tests, concrete was with and without crimped steel fibers of ratio 1% by volume.In investigating high-velocity impact strength, the decrease in projectile penetration depth was (5-17%) and the scabbing area reduced (15-35%) over reference concrete.In studying PMC including 1% by volume steel fibers, an additional increase was observed in all properties. The increases were quite significant in high-velocity impact strengths. Further reduction was recorded in scabbing area of (64-95%) and penetration depth reduced (28-39%) over control specimens. The fragmentations were reduced also. The range of corresponding compressive was (48-64)MPa ,of splitting tensile strength (4.2-7.8) MPa, and of flexural strength (5-8) MP
The object of this paper was reduced the heat transferred quantities from or to internal building space by covering it's external walls with many materials, therefore, the researcher build the (1x1x2) m room sample at 3rd floor for building in Baghdad city (L = 33.2 N°), and (1x2)m wall has East orientation , while the other surfaces were insulated by 200 mm styropor sheets, and using Air – Conditioner 0.5 Ton of refrigeration to afford the standard thermal comfort. The researcher found that, the metal sheet painted with thermal plastic paint with 10 mm thermal insulation used as a cover layer for ordinary wall saved 57% from electrical energy consumption in Air-Conditioner, while used that material without insulation layer gives 46.2% , hollow plastic board (for decorative used) gives 42.5% , hollow faced brick with thermal insulation gives 40.22%, solid flooring brick with thermal insulation gives 39.5% , colour metal sheets with air – gap gives 36.4%, asbestos – cement board coated by reflective aluminum paint gives 34%, the ceramic with thermal insulation gives 31.9%, while all the material – marble , porcelene , hallan stone , fiberglass sheets with 10 mm thermal insulation will gives the electrical energy reduction percentage less than 30% .
The researches in Iraq has expanded in the field of material technology involving the properties of the light weight concrete using natural aggregate aviable in westran of Iraq. Researches work on porcelinite concrete has been carried out in several Iraqi Universities. The study is deals with mechanical properties of porcelinite aggregate concrete by casting (273) different specimens. These properties are, compressive strength, flexurale strength, splitting strength, static modulus of elasticity and absorption. The results indicated that the structural light weight aggregate concrete produced from local porcelinite aggregate is suitable to used as a structural concrete, it can produce structural light weight concrete of compressive strength varies from (23.0 to 29.8) MPa with the density ranges from (1745 to 1855) kg/m3, by using cement content about (550 and 650) kg/m3.Such concrete exhibited good mechanical properties. It gave the values of splitting tensile strength, modulus of rupture and modulus of elasticity, 75%, 90% and 60% from those of normal weight concrete respectively owning the same compressive strength and meeting the requirement of ACI-213
Housing represents a major world wide problem, especially for developing countries. It is essential to construct suitable housing units that are appropriate for the continuing population increase. Many countries have applied construction (policies) that depended on the available material and human resources. These schemes aim at producing the greatest number of dwelling units that are suitable for the people who do not own units. The aim of this research is the scope of low cost dwelling units in general, and through the reduction of roofing cost. The objective of the research, Economical feasibility study for production precast units (ferro cement units) for roofs of low cost dwelling and compare the cost of the proposed system With other conventional roofing systems: roofing by (jack arching) and reinforced concrete. Fifteen units of Ferrocement with square shape and three different dimensions were cast and tested for load test, tensile strength, compressive strength and bending. The optimized dimensions were (750*750*20)mm and the capacity ranges from (13 to 17.7)KNM2.The cost of (1m2 ) of these units was (38292.4)I.DM2 while the cost of (1m2 ) reinforced concrete (58534.94(I.D and (51062.7) I.DM2 for (jack arching)
The purpose of this paper is to investigate the relationship between the Ultrasonic Pulse Velocity (UPV) and the compressive strength and the flexural strength of hardened concrete when subjected to different concentrations of sulfate attacks. The specimens used in the studies were made of concrete with different water-cement ratios (w/c). The UPV measurement and compressive and flexural strengths tests were carried out for concrete specimens of ages (4-40) days. The experimental results show that the relationship between UPV and the compressive and the flexural strengths of concrete is significantly influenced by age and the concentration of sulfate attack. The UPV and the compressive strength of concrete grow with age, but the growth rate varies with w/c ratio. It is found that with the same concentration of sulfate attack, a clear relationship curve can be drawn to describe the UPV and compressive and flexural strengths of hardened concrete. This paper presents the UPV-strength relationship curves for concrete having different (w/c) ratios subjected to different concentrations of sulfate attack. These curves are thought to be suitable for prediction of hardened concrete strength with a measured UPV value when sulfate attack is considered. It is concluded that the UPV increases with the increase of the compressive and flexural strength. The observed range for UPV was (3.5 to 4.75 km/sec) corresponds to (24 to 28.5 N/mm2) for compressive strength and to (4.6 to 6.5 N/mm2) for flexural strength. The UPV decreases with the increase of the concentration of sulfate exposure. The obtained maximum reduction in UPV was 31.6% with respect to the control spacemen at age of 40 days.
This research include the study of flexural behavior of polymer modified concrete beams containing waste plastic fiber (WPF). Fifteen reinforced concrete beams are moulded of (100*150*1300) mm dimension with different steel reinforcement ratio (ρ). These steel reinforcement ratio were (0.0038, 0.0207 & 0.0262). Styrene Butadine Rubber (SBR) was added as cement replacement by weight equal to (5%). Reinforced concrete beams classified in to five groups, each contains three beams with different (ρ) value. The first group conducted of reference concrete mix , the second group made with SBR modified concrete, while the three remaining groups were make by PMC containing (WPF) with volumetric ratio equal to (0.75, 1.25 & 1.75)%. This study includes compressive and flexural tests for concrete which was used in this research, load deflection relationships, the moment at mid-span with deflection and ductility were established. The results prove that, polymer modified concrete wich content waste plastic fiber has compressive and flexural strengths more than reference mixes as well as the PMC beams wich content waste plastic fiber have a stiffer response in terms of structural behaviour, more ductility and lower cracking deflection than those made by reference concretes and that refer to good role of styrene Butadiene Rubber (SBR) polymer and plastic fiber on the properties and behaviour of reinforced concrete beams.
Ferrocement is a type of concrete made of mortar with different wire meshes. It has wide and varied applications in addition to its strength and durability. This research aims to combine ferrocement and sustainability, as over time, the consumption of plastics, especially plastic bottles, has increased and has serious negative effects if buried, burned, or chemically analyzed. Therefore, this research aims to benefit from this plastic waste and introduce it into the construction field by using plastic waste fibers in the concrete mixture instead of cement at a rate of 0.5% and 1% by volume. This research studied the mechanical properties of nine samples of ferrocement beams with dimensions of 1200 × 200 × 150 mm3. A longitudinal hole with a diameter of 50 mm was drilled in different places of the beams and filled with lightweight concrete to facilitate the use of the hole in service passes when drilled, with a study of the initial cracking loads and the resulting deflection in addition to the failure modes and the deflection resulting from the maximum load. The results showed an improvement in load resistance with an improvement in deflection at the maximum load, In addition to an increase in the improvement of Toughness and Stiffness of ferrocement beams.
Abstract This research studies the effect of adding steel fiber in two percentage 0.5% and 1% by volume on plain structural lightweight concrete (SLWC) produced by using crushed bricks as coarse lightweight aggregates (LWA) in a lightweight concrete mix designed according to ACI committee 211-2-82 with mix proportion 1:1.12 :3.35 by volume .The wc equal to 0.5 and cement content 550 kgm3. Different tests where performed for fresh and hardened SLWC such slump test ,fresh and hardened unit weight ,compressive strength and two indirect tests of tensile strength (splitting tensile and flexural strength). The results demonstrated that the effect of addition of steel fiber was more pronounced on the tensile strength of SLWC than the compressive strength of such concrete .The maximum increase of compressive ,splitting tensile and flexural strengths at 28-days were 38.8,77.12 and 111.2 % in the SLWC containing 1% fiber. On the other hand the rate of strength gain between 3 and 28 days was constant on compressive strength of plain concrete and that containing steel fiber while this rate was clearly increase on tensile strength especially flexural strength.
The present study, concern about an experimental work to study the stress-strain relationship of steel-fiber reinforced polymer modified concrete under compression. Four different mixes with weight proportions of (1:2:4) were used as; normal weight concrete (NC), polymer modified concrete (PMC) with (10%) of cement weight and two mixes of steel-fiber polymer modified concrete with (1%) and (2%) volume fraction of steel fiber, (SMPC). The influences of polymer and fiber addition on peak stress, strain at peak stress and the stress-strain curve were investigated for concrete mixes used. For all selected mixes, cubes (150×150×150mm) were made for compressive strength test at (28) days while stress-strain test was caried out on cylinders (150 mm 300 mm) at the same age. Results showed an improvement in compressive strength of polymer modified concrete (PMC) over reference mix, the maximum increase of it was (13.2 %) at age of (28) days. There is also an increase in compressive strength with increasing of steel fibers content with comparison to normal concrete, the maximum increases of it were (19.6% and 25.2%) of mixes with 1% and 2% fiber content by volume respectively. In terms of modulus of elasticity, the addition of polymer and the presence of fibers cause a significant increase in it. The peak of stress- strain curve for normal strength concrete (Mix No.1) was linear whereas it was more sharp for the other mixes. The behaviour of normal strength concrete (Mix No.1) was linear up to 20 % of ultimate strength, while for the mixes with the higher strength i.e. polymer modified concrete and fibers reinforced concrete (Mixes No.2, 3 and 4) the linear portion increases up to about 50 % of ultimate strength
This study is the second stage of the paper “Study the Effect of Rubber Silicon on Physical Properties of Asphalt Cement”. This study took the effect of additives on asphalt mixture performance. Asphalt mixture has been designed by Marshall method for determining the optimum asphalt content and geophysics properties of mix according to ASTM (D- 1559 ). Rubber silicon at different percentage (1%, 2%, 3% and 5%) was added to asphalt binder and three specimens of asphalt rubber silicon mixture (ARSM) are prepared and evaluating according to Marshall method. Diametric tensile creep test ASTM (D-1075) at 60 Co used to evaluating permanent deformation and modulus of elasticity for ARSM. The study shown that the Rubber-Silicon has more effects increasing the marshal stability, air voids, and reducing the flow and bulk density compared with the original mix.. Increase the flexibility properties of the mix and this appear from reducing the permeate deformation at test temperature (60C), the reduction percent is about (30 to 70)%
The use of textile reinforcement made from non-corrosive materials, such as carbon and glass can reduce the required concrete material; this is known as Textile Reinforced Concrete (TRC). This study deals with plate specimens having dimension of 500×500×40mm tested under impact load at 28 and 90 days age under two conditions of ends, simply supported and fixed. Cement mortar with about 60 MPa, 7cm cube compressive strength at 28 days was designed for casting the plates. Plate specimens were divided into four groups, they consist of reference plates (no reinforcement) and plates reinforced with 3D glass fabric having three different thicknesses 6, 10 and 15mm. The results indicate that using 3D textile glass fabric cause an increase in number of blows, reduce in final stage deflection, an improvement in toughness and energy absorption under impact loads. Using 3D textile glass fiber with 10mm thickness gave higher number of blows for 28 and 90 days as compared with 6 and 15 mm. Plates with slice 6mm 3D textile glass fiber in two way reinforced has significantly enhancement in number of blows, the improvement was about (80 - 125%) and (128.5- 114. 3%) for 28 and 90 days respectively. The specimens showed increase in the energy absorption, besides the number and width of cracks was reduced and only few cracks are propagated up to the edge of the plates.
This research includes study of the of effect of adding sulphur, which is obtained from Samrraa factory on the properties of concrete like compressive strength, flexural strength and splitting tensile strength. The concrete mixes were: (1:8.5:8.5:7), (1:8.5:8.5:9), (1:8.5:8.5:12) and (1:1.5:3:0) (cement: sand: gravel: sulphur) respectively. The results refer to increasing of compressive strength , flexural strength and splitting tensile strength with increasing of sulphur ratio but increasing decreased at age (28)day with respect to ordinary concrete (sulphur ratio=0%).
This research includes the study of improving impact resistance of concrete using styrene butadiene rubber (SBR) with different weight ratios of polymer to cement 3%, 5% and 10%. Two series of polymer modified concrete (PMC) were produced the first level I with moderate compressive strength and the other level II with higher compressive strength. Cubes, prisms and panels were made as follows: Results showed an improvement in impact resistance of polymer modified concrete (PMC) over reference concrete in low-velocity and high-velocity impact properties. In conducting low-velocity impact tests, method of repeated falling mass was used: 1300gm steel ball falling freely from three heights 2400mm, 1200mm and 830mm. In high-velocity impact tests, shooting of 7.62mm bullets was applied to slab specimens from distance of 15m. The improvements were significant in low velocity impact resistance. The maximum increases were (33.33%, 75% and 83.33%) at ultimate failure for falling mass heights 2400mm, 1200mm and 830mm respectively. In high-velocity impact strength tests, maximum reductions recorded in spalling area were (18.5% and 27%) for polymer modified concrete (level I) with moderate compressive strength and polymer modified concrete (level II) with higher compressive strength.Maximum reductions recorded in scabbing area were (11.42% and 35.6%) for polymer modified concrete (level I) with moderate compressive strength and polymer modified concrete (level II) with higher compressive strength, respectively.
This research includes studying the possibility of producing a new kind of No-fines concrete by replacing granules of coarse aggregates with grains results from the fragmentation of industrial waste of polystyrene. This replacing were with different volumetric proportions of coarse aggregate, and theses volumetric ratios were equal to (5%, 10%, 15% and 25%). Waste plastic fibers (WPFs) resulting from cutting of soft drinks bottles were added for strengthening this new kind of concrete. Mixing ratio was equal to (1:5) (cement: coarse aggregate) by weight. One reference mix was produced for comparative purpose. Compressive strength, flexural strength and density tests were conducted, it was examined three samples of each examination and taking the average. Compressive strength values of the new sustainable concrete were ranged from 10 MPa to 12.4 MPa at age of test equal to 28 days, while the average value of the density of this concrete at the same age reaches 1930 kg/m3. This average value of modulus of rupture was equal to 2.36 MPa at 28-day age test.
Abstract:-This investigation studies the mechanical characteristics of carbon fiber reinforcedlight weight aggregate concrete, containing different percentages of fiber. The effect ofusing high range water reducing agent (SP) with 8% silica fume (SF) and 8% highreactivity Metakaolin (HRM), as a partial replacement by weight of cement, on thebehavior of (LWA) concrete is also studied.This investigation was carried out using several tests. These tests were workability freshand hardened density, compressive strength, splitting tensile strength and modulus ofrupture. Tests were performed for specimens at ages of (7,28,60,90 and 180) days . Thetest results indicated that the inclusion of carbon fiber to the light weight concrete mix didnot affect the compressive strength significantly, while the splitting tensile strength andthe modulus of rupture were improved significantly. The addition of silica fume andmetakaolin improves the compressive, splitting tensile , and modulus of rupture strengthsof carbon fiber light weight concrete. The average improvement was about (26.5%, 71%and 73 %) respectively for carbon fiber LWA concrete containing silica fume and (28%,72% and 75%) respectively for carbon fiber LWA concrete containing high reactivitymetakaolin.
One of the most popular non- destructive techniques is ultrasonic pulse velocity (UPV) which used in assessment of concrete properties. A statistical experimental program was carried out in the present study to establish an accurate relation between the UPV and the concrete compressive strength. The program involved testing of concrete cubes cast with specified test variables. The variables are the age and density of concrete. In this research, all the samples were tested by direct ultrasonic pulse velocity (DUPV) and surface ultrasonic pulse velocity (SUPV) to measure the wave velocity in concrete and the compressive strength for each sample. An experimental study was conducted to compare between the velocities of ultrasonic waves that transmitted along the two paths; direct and indirect. A total of more than 150 cubes having dimensions of 150 mm side were prepared to conduct both non-destructive and the compressive strength (destructive testing). The results from experimental program were used as input data in a statistical program (SPSS) to predict the best equation, which can represent the relation between the UPV (direct, indirect), and compressive strength, a linear equation is proposed for this purpose. The UPV measurement and compressive strength tests were carried out at the concrete age of 7, 28, 56 days. A relationship curves were drawn between DUPV, SUPV, compressive strength and density. The mixes composition in this study consists of ordinary Portland cement, fine sand, gravel, super-plasticizer, and water. All the specimens were under (20) Cº. The statistical analysis revealed that the possibility in evaluating the properties of the concrete by using direct and indirect wave velocities
The super fine materials constitute that portion of mineral filler finer than 10 microns. The effectiveness of these materials comes from their relation with asphalt film thickness. Asphalt cement grade (40-50) has been used. Nibaay course aggregate and Thmail fine aggregate were combined to achieve the aggregate gradation confirms with the Iraqi Standard Specifications for dense graded mix. Six different types of filler from five locally different sources in Iraq had used and subjected to grain size distribution, specific gravity and chemical composition tests. To study the effect of super fine materials on the performance of HMA mixture, Marshall stiffness, Indirect tensile strength, Moisture susceptibility and Creep tests have been made. Statistical analysis for results has been made. The conclusions referred to the importance of super fine materials due to their effect on HMA concrete properties.