This study was conducted to examine the impact of plastic fibers (WPFs) in an effort to improve some of the features of self-compacting concrete (SCC) using Iraqi raw materials. Waste polyethylene terephthalate fibers (waste PET fibers) from used beverage bottles were added. Some tests were carried out to determine the effects of adding WPFs on the fresh properties of new concrete, while additional tests examined the mechanical properties of hardened concrete. Because of this, self-compacting concrete blends were created with a constant water-to-binder ratio of 0.32 and a binder content of 525 kg/m3. The designated plastic fiber percentages contents were 0%, 0.5%, 0.75%, and 1% of mix volume. Self-compacting concrete mixtures' fresh characteristics were assessed for slump flow diameter, T50 slump flow concurrently, V-funnel flow concurrently, and L-box height ratio. The 28-day density, compressive strengths and flexural strength of self-compacting concretes were also measured. The use of plastic waste fibers had a slight effect on reducing the density of the produced concrete and a negative effect on the fresh properties. The compressive strengths were improved by using WPFs, with the maximum improvement equal to (11.065%) when compared to those made from the reference mix
Fresh and hardened properties of self-compacting concrete was experimentally examined by replacing different percentages of cement by soft clay powder, which resulting from crushing the wastes of clay bricks. Three percentages (5%, 10%, and 15%) of cement were replaced with clay powder to study their effect on the properties of cement mortar and concrete of Grade (C35) in both fresh and hardened states. It was found that development rates of the compressive and tensile strengths for the mortar between ages of 7 to 28 days, decreased with increasing the percentage of the clay powder. Compared to the mix without clay powder, it was found that replacing (5%) from the cement causes a significant increase in the workability of the self-compacting concrete and the properties of the resulting hardened concrete such as compressive strength, tensile strength, and modulus of elasticity. While using (10%) and (15%) of the clay powder causes a significant decrease in the workability of the fresh concrete and the properties of the hardened concrete compared to mix without clay powder.
This study presents an experimental research of Self-Compacting Concrete (SCC) properties containing waste plastic fibers (WPF). Adding waste plastics which resulting from cutting PET bottles as fibers to SCC with aspect ratio (l/d) equal to (28). To illustrate the effects of WPFs on the SCC, the current study was divided into two parts, the first part shows the effect of adding plastic fibers on the properties of fresh SCC, which include the ability flow, spread, passing and resistance to segregation, and the second part to evaluate the properties of hardened (mechanical) destructive and non-destructive, which include compression strength, flexural strength and ultrasonic pulse velocity test. One reference concrete mix was conducted and eight mixes contain WPF has been producing self-compacting concrete mixers containing a different volumetric ratio of plastic fibers (Vf) % percentages (0.25, 0.5, 0.75, 1, 1.25, 1.5, 1.75, 2) %. Three cubes samples were prepared for testing the compressive strength, three prisms were prepared for the test modules of rupture, one cylinder were prepared testing the modulus of elasticity. The experiments show that adding plastic fibers to SCC leads to an increase in the compression strength and modulus of rupture at 28-day as follows (42.30)% and (73.12)% respectively for mix ratio (1.5)% in comparison with the reference mix, which represent the best ratio of fibers, as such the results of testing the fresh concrete containing waste fibers showed that adding these fibers led a reduction in workability for SCC.
This paper presents and discuses some properties of self-compacting concrete SCC containing optimum contents of different types of cement replacement materials CRMs like fly ah, silica fume and limestone powder. The purpose is to evaluate the performance of SCC mixtures to choose the best one for strengthening purposes of corroded reinforcement concrete beams. In a preliminary work, the theoretical optimum contents of the above materials were specified using statistical program (Minitab) and they were verified experimentally. This verification based on checking fresh properties such as slump flow, T500, L-box and segregation resistance as well as compressive strength. The optimum contents of CRMs: 14% fly ash, 19% limestone, 18% silica fume plus fly ash and 11% silica fume were selected and studied. Compressive, tensile, and flexural strengths were examined, as well as the modulus of elasticity, water absorption and porosity (which reflect the related durability properties) were examined. Test results show that the optimum verified theoretical percentage of a combination of fly ash and silica fume, at 18% by weight of cement with a fixed water-binder ratio of 0.33 showed the best overall performance. It was deduced that this SCC mix gave the highest mechanical properties and the lowest porosity and water absorption. For example, the compressive strength increased by 36.25% as compared to SCC mix containing limestone powder. Further, the porosity and water absorption decreased by 120.8% and 164% respectively as compared to the above same SCC mix. Thus, it could be used for strengthening purpose of corroded RC beams.
The aim of this study is to develop Lightweight self-compacting concrete (LWSCC) mixtures using locally sourced waste materials such as Expanded Polystyrene Beads (EPS) and Waste Plastic Fibers (WPFs) which are all available abundantly available in Republic of Iraq at little or no cost. The fresh, hardened and mechanical properties of these LWSCC were studied, followed by results analysis. Five different mixes of LWSCC were prepared in term of WPF content (0.25, 0.5, 0.75, 1.0, and 1.25 %), in addition to the control mix (R mix) and lightweight concrete (E mix) made of EPS content as a replacement of coarse aggregate. The study showed that the LWSCC produced with these waste materials were decreased the density (lightweight) of the concrete mixes as EPS tend to form more clumps, absorb water and make the mix dry. Therefore, concrete mixtures were adjusted accordingly to be able to offset the workability caused by the addition of EPS. The increase in WPF content decreased the workability due to clumping that occurred in the mixing phase. The analysis of mechanical properties of the LWSCFRC specimens revealed that there was not much improvement. While LWSCC with 100% of EPS replacement as coarse aggregates and 1.25% WPFs provides the best flexural toughness performance
The problem of discarded tires has received a lot of attention from many authors. Incorporation of rubber aggregate recycled from waste tires is one of the solutions to this issue. This research is based on evaluating fresh and hardened properties such as slump flow, T500, segregation resistance, and L-box tests, compressive strength, impact resistance, and flexural toughness. Rubber aggregate replacements in the self-compact concrete mixes was 10% by volume of fine aggregate. Additionally, both PET and steel fibers are utilized at a volume rate of 0.25%.The outcomes indicate that introducing rubber declines rheological and hardened properties, whereas incorporating hybrid fibers enhances hardened properties such as compressive strength, impact energy, and flexural toughness. The best increase impact energy was obtained at roughly 166.6% when 0.25% hybrid fibers and 10% rubber were used. 74.21 was the greatest increase in flexural toughness when 0.25% hybrid fibers (SCCH3) were used. As for the compressive strength, it was the highest by about 11%.
This main aim of this study is evaluate wide range of fresh and hardened properties of sustainable self-compacting concrete containing various types of Cement Replacement Materials with optimum contents of Polyethylene Terephthalate PET waste plastic as fibers and fine aggregate replacement. This is to evaluate effect of the two forms of PET and to determine the best CRMs could be used with sustainable SCC. such as limestone, glass powder and fly ash with high replacement rate of 70% by weight of cement were used while fourth one (kaolin) was used with replacement rate of 20%. PET fibers were added to SCC with an aspect ratio of 24.4 and 0.7% volume fraction whereas fine aggregate partially replaced by 4% of waste plastic. Four reference mixtures contained FA, LP, GP and KA only, same four mixtures contained 0.7% PET fibers by volume, and the other same four mixtures contained 4% PET fine aggregate by volume. The obtained results all tested fresh properties, which include slump flow, T500, L-Box and segregation resistance were within the limits of the specification reported in EFNERC guidelines. Further, the forms PET have an adverse effect fresh properties of SCC. As for hardened properties (compressive strength, splitting tensile strength, flexural strength and impact strength). Further, this produced type of SCC showed an range of compressive strength (15.2-31.64 MPa) at 28 days. It can be from the current study the best CRMs to be used in SCC containing PET wastes was FA in terms of most tested properties.
In this study, eight rectangular reinforced concrete beams strengthened by bottom steel plates firmly interconnected to them by headed-stud shear connectors are manufactured using self compacting concrete and tested up to failure under two point loads to demonstrate the effect of steel-plate thicknesses, lengths, and the shear-connector distributions on the behavior, ductility and strength of this type of beams. A trial mix conforming to the EFNARC Constraints had been successfully carried out to satisfy the three fresh tests of SCC, these tests are flowability, passing ability and segregation resistance. The results show that there is a substantial improvement in the flexural resistance, increasing the flexural stiffness and decreasing the ductility ratio due to thickening steel plate, On contrary, increasing the spacing between shear connectors to 50% had slight effect on the flexural resistance, but subsequent increase of their spacing to 100% had seriously lowered that resistance, The spacing between shear connectors has a primary effect on the average flexural stiffness and ductility ratio. In regard to the steel plate length, its shortening has reduced the flexural resistance significantly, decreased the average flexural stiffness and had increased the ductility ratio. The experimentally determined ultimate flexural strength had been compared with its corresponding one computed by the "Strength Method" using ACI requirements where high agreement gained between them due to the nearly perfect interaction provided by SCC. The eight composite beams had also been analyzed by the non-linear three dimensional Finite Element Analysis employing ANSYS program (release 12.1),where high agreement is achieved compared with experimental results.
AbstractThis study aims to investigate the properties of SCC produced by locally availablematerials , and attempts have been made to increase the range of grading of fineaggregate, with fineness modulus ranging from (1.5 to 4.1) , and to study the effect of themaximum size of coarse aggregate . It also aims to study the influence of High ReactivityMetakaolin (HRM) as a partial replacement by weight of cement on the properties of freshand hardened SCC, 24 different mixes of SCC are prepared .8 mixes are considered asReference mixes which are used for comparison purposes. To determine the workability,different test methods were adopted such as slump flow, V-funnel, and L-box tests. Whenfineness modulus of fine aggregate and maximum size of coarse aggregate increase,flowability, passing ability and segregation resistance decrease as compared with smallmaximum size of aggregate and other fineness modulus. Further more, the inclusion of10% HRM as a partial replacement by weight of cement leads to decrease flow ability andincrease of viscosity. The fineness modulus (3.1) of fine aggregate gives better resultsthan other fineness modulus. The results obtained from this study, also show that it ispossible to produce SCC from local available materials which satisfy the requirement ofthis type of concrete. Moreover, the results show the possibility of using different gradingof fine aggregate with fineness modulus ranging from (1.5 to 4.1) and the effect ofchange in fineness modulus is not significant on hardened concrete properties , while it ismore significant on fresh concrete properties .