The principal objective of this paper is to investigation the experimental of the flexural behavior of strengthened and repaired reinforced concrete slabs with ferrocement tension zone. The result of tests on 10 simply supported one way slabs were presented, at which include 1control slab, 5strengthened slabs and 4repaired one way slabs. In the strengthened slabs, the cover of the control slab replacing with ferrocement cover, cold joint between ferrocement layer and the slab, connection type between the ferrocement layer and the slab, on the ultimate load, first crack load, the mid span-deflection, crack width and spacing were examined. In the repaired part the slabs were loaded to (55 %) of measured ultimate load of control slab, the effect of the thickness and number of wire mesh layers on crack pattern, mid span deflection and ultimate load was examined. In the repaired part the slabs were loaded to (55 %) of measured ultimate load of control slab, effect of the number of wire mesh layers of ferrocement on the mid span deflection, ultimate load and crack pattern was examined. The experimental results of strengthened and repaired slabs indicate that; the ultimate loads and mid span deflection were more effected by using ferrocement mortar at tension zone. The increase in ultimate load (8.2-18%) for strengthen slab and (9.1-17.3%) for repaired slab respect to the control slab.
Ferrocement is a type of concrete made of mortar with different wire meshes. It has wide and varied applications in addition to its strength and durability. This research aims to combine ferrocement and sustainability, as over time, the consumption of plastics, especially plastic bottles, has increased and has serious negative effects if buried, burned, or chemically analyzed. Therefore, this research aims to benefit from this plastic waste and introduce it into the construction field by using plastic waste fibers in the concrete mixture instead of cement at a rate of 0.5% and 1% by volume. This research studied the mechanical properties of nine samples of ferrocement beams with dimensions of 1200 × 200 × 150 mm3. A longitudinal hole with a diameter of 50 mm was drilled in different places of the beams and filled with lightweight concrete to facilitate the use of the hole in service passes when drilled, with a study of the initial cracking loads and the resulting deflection in addition to the failure modes and the deflection resulting from the maximum load. The results showed an improvement in load resistance with an improvement in deflection at the maximum load, In addition to an increase in the improvement of Toughness and Stiffness of ferrocement beams.
This study introduce a review on structural behavior of different structural elements such as beams, slabs, column….etc, under different type of loading. Through this review one can see the effectiveness of using ferrocement in casing slabs, beams subjecting to bending or impact load. Also the ferrocement make an essential role in strengthening of damage columns and beams.
This paper presents the experimental results of eight slabs made of Ferrocement. All specimens were )700mm (long, )300mm (wide and )50mm (thick. These specimens were divided into two groups (The first group has four specimens coursed of normal sand gradient and in the other four specimens, the sand that passing from sieve No. 8 was neglected), to investigate behavior of slabs under bending effect and studying the cracks that generated after bending then, comparing the results between these two groups. A thin square welded wire mesh was used as reinforcement. The number of wire mesh layers was varied between 0 to 3 layers. Ultrasonic Pulse Velocity (UPV) Test was used to detect the cracks. The results showed that there was a slight rise in bending for first group slabs compared with second group slabs. Maximum bending strength was achieved for both slab groups with 3 layers of wire mesh. it was shown that there was a significant convergence in the load values required to cause appearing of the first crack and final failure for the two groups. The percentage of ultimate load between slab reinforced with 3 layers and without reinforcement was (25.27%) for the first group, while the increase in ultimate load for a specimen that reinforced with 3 layers was (24.16%) compared to specimen without reinforcement for the same group. On the other hand, the results showed an improvement in the performance of the second group slabs due to its resistance to appearing of cracks resulted from bending. The percentage of increasing cracks after bending for the unreinforced specimen in group 1 was (9%) compared with the unreinforced slab in group 2. Whereas the numbers of cracks number in slab reinforced with 1 and 2 layers in the second group were less than slabs with 1 and 2 layers in the first group about (8.86 %) and (7.77%), respectively. While this percentage for a specimen with 3 layers in group 2 was about (8.62%) less compared to the specimen with 3 layers in group 1..
Housing represents a major world wide problem, especially for developing countries. It is essential to construct suitable housing units that are appropriate for the continuing population increase. Many countries have applied construction (policies) that depended on the available material and human resources. These schemes aim at producing the greatest number of dwelling units that are suitable for the people who do not own units. The aim of this research is the scope of low cost dwelling units in general, and through the reduction of roofing cost. The objective of the research, Economical feasibility study for production precast units (ferro cement units) for roofs of low cost dwelling and compare the cost of the proposed system With other conventional roofing systems: roofing by (jack arching) and reinforced concrete. Fifteen units of Ferrocement with square shape and three different dimensions were cast and tested for load test, tensile strength, compressive strength and bending. The optimized dimensions were (750*750*20)mm and the capacity ranges from (13 to 17.7)KNM2.The cost of (1m2 ) of these units was (38292.4)I.DM2 while the cost of (1m2 ) reinforced concrete (58534.94(I.D and (51062.7) I.DM2 for (jack arching)